Chemical Composition, weight % Carbon: 0.08 Max Manganese: 1.50 Max Silicon: 2.00 Max Phosphorus: 0.04 Max Sulfur: 0.04 Max Chromium: 18.0-21.0 Nickel: 9.0-12.0 Molybdenum: 2.0-3.0 Tensile Requirements Tensile Strength, ksi: 70 Min Yield Strength, ksi: 30 Min Elongation in 2 in.: 30% Min Similar Specifications Cast UNS: J92900 Wrought UNS: S31600 Wrought Grade: 316
Chemical Composition, weight % Carbon: 0.20 Max Manganese: 1.50 Max Silicon: 2.00 Max Phosphorus: 0.04 Max Sulfur: 0.04 Max Chromium: 18.0-21.0 Nickel: 8.0-11.0 Tensile Requirements Tensile Strength, ksi: 70 Min Yield Strength, ksi: 30 Min Elongation in 2 in.: 30% Min Similar Specifications Cast UNS: J92602 Wrought UNS: S30200 Wrought Grade: 302
Chemical Composition, weight % Carbon: 0.12 Max Manganese: 1.50 Max Silicon: 2.00 Max Phosphorus: 0.04 Max Sulfur: 0.04 Max Chromium: 20.0-23.0 Nickel: 10.0-13.0 Tensile Requirements Tensile Strength, ksi: 70 Min Yield Strength, ksi: 28 Min Elongation in 2 in.: 35% Min Similar Specifications Cast UNS: J93001
Chemical Composition, weight % Carbon: 0.08 Max Manganese: 1.50 Max Silicon: 2.00 Max Phosphorus: 0.04 Max Sulfur: 0.04 Max Chromium: 18.0-21.0 Nickel: 8.0-11.0 Tensile Requirements Tensile Strength, ksi: 70 Min Yield Strength, ksi: 30 Min Elongation in 2 in.: 35% Min Similar Specifications Cast UNS: J92600 Wrought UNS: S30400 Wrought Grade: 304
Chemical Composition, weight % Carbon: 2.0-3.3 Manganese: 2.0 Max Silicon: 1.5 Max Nickel: 2.5 Max Chromium: 23.0-30.0 Molybdenum: 3.0 Max Copper: 1.2 Max Hardness Requirements As Cast: 46 HRC Min. Hardened: 56 HRC Min.
Chemical Composition, weight % Carbon: 2.0-3.3 Manganese: 2.0 Max Silicon: 1.0-2.2 Nickel: 2.5 Max Chromium: 18.0-23.0 Molybdenum: 3.0 Max Copper: 1.2 Max Hardness Requirements As Cast: 46 HRC Min. Hardened: 56 HRC Min.
Chemical Composition, weight % Carbon: 2.0-3.3 Manganese: 2.0 Max Silicon: 1.5 Max Nickel: 2.5 Max Chromium: 14.0-18.0 Molybdenum: 3.0 Max Copper: 1.2 Max Hardness Requirements As Cast: 46 HRC Min. Hardened: 56 HRC Min.
Chemical Composition, weight % Carbon: 2.0-3.3 Manganese: 2.0 Max Silicon: 1.5 Max Nickel: 2.5 Max Chromium: 11.0-14.0 Molybdenum: 3.0 Max Copper: 1.2 Max Hardness Requirements As Cast: 53 HRC Min. Hardened: 56 HRC Min.
Chemical Composition, weight % Carbon: 2.5-3.6 Manganese: 2.0 Max Silicon: 2.0 Max Nickel: 4.5-7.0 Chromium: 7.0-11.0 Molybdenum: 1.5 Max Hardness Requirements As Cast: 50 HRC Min. Hardened: 56 HRC Min.